Is a ready mix coating prepared bd using special grains and fillers to obtain requried texture.It has high coating capacity and adherence to sub base.resists to U.V abrasion and impact.Discoloring and carck formation is not observed.Vapor is diffused to outside.It is gives travertine texture effect.Produced in different colors.

Is packed in 25 kg plastic buckets.

Is used to coat plaster concrete and other mineral subbases, Self supporting acrylic painted surfaces and cemexs COMPLETE HEAT, INSULATED SURFACES as well.To obtain textured look.Finishing is made teraks.

2,8-3,2 KG/m2for 2mm Thick Coat (Fine)
3,5-3,7 KG / m2 for 3 mm Coat (Coarse)

In unopened plastic buckets, under normal temperature shelf life is 1 year.(Should be protected from frost and contact with sunshine.)

Subsurfarce should be: sound, celan, and free from dirt , dust and loose particles.Blisters should be cleaned by brush,grinder or rasp.
Newly plastered surfaces should be left to dry for 2 to 4 weeks.

All kind of subbase should be primed by Latex-Pm and to dry minimum 6 hours.Latex,Pm is applied on by steel trowel.Right after decorative effect is formed by round, horizontal or vertical movements of a plastic trowel.

Temperature should not not drop below 5°C following 24 hours.
Touch dry:1-2 hours at 21°C
Final dry:24 hours.
Tools should be washed with clean water.It is not applied to horizontal and sloped areas more than 45°C, Care should be paid to strong windy and very hot days, under direct sun light.Large surfaces should be protected from cold joints by sepration bandages.

TECHINICAL CHARACTERISTIC:
• STRIPPING RESISTANCE : Dry >2,5 kgf
• Wet-Dry >2 kgf
• Frost-thaw >2 kgf
• WATER ABSORBTION : < 0,5 Kg / cm2<h 0,5
• PH : 8-9
• VAPOUR DIFFUSION : 0,5 m-1
• REFERRED STANDARD :TS 7847